PbSnTe crystals were grown using the horizontal vapor phase growth (HVPG) method with growth temperature of 1000 C and 1200 C and growth time of four and eight hours where its surface morphology and elemental compositions were analyzed using the Phenom ProX Desktop SEM with EDS. The effect of the interaction term between growth temperature and growth time with respect to the figure of merit ZT was analyzed using the Design of Expert software, where the p-values obtained were significant. At room temperature, the high figure of merit was approximately 0.084, which can be correlated from the formation of the cubic crystals that were grown at 1200 C for four hours.
Keywords: Crystal structure, HVPG, PbSnTe, Thermoelectrics material.[1] P. Dziawa et al., “Topological crystalline insulator states in Pb1−xSnx Se,” Nat. Mater., vol. 11, no. September, pp. 1023–1027, 2012.
[2] J. He et al., “Strong phonon scattering by layer structured PbSnS2 in PbTe based thermoelectric materials,” Adv. Mater., vol. 24, no. 32, pp. 4440–4444, 2012.
[3] C. Gayner and K. K. Kar, “Recent advances in thermoelectric materials,” Prog. Mater. Sci., vol. 83, pp. 330– 382, 2016.
[4] H. J. Goldsmid, Introduction to Thermoelectricity, vol. 121. Berlin, Heidelberg: Springer Berlin Heidelberg, 2010.
[5] C. C. Lin, D. Ginting, R. Lydia, M. H. Lee, and J. S. Rhyee, “Thermoelectric properties and extremely low lattice thermal conductivity in p-type Bismuth Tellurides by Pb-doping and PbTe precipitation,” J. Alloys Compd., vol. 671, pp. 538–544, 2016.
[6] J.-F. Li, W.-S. Liu, L.-D. Zhao, and M. Zhou, “High Performance nanostructured thermoelectric materials,” NPG Asia Mater., vol. 2, no. 4, pp. 152–158, 2010.
[7] E. Xu et al., “Enhanced thermoelectric properties of topological crystalline insulator PbSnTe nanowires grown by vapor transport,” Nano Res., vol. 9, no. 3, pp. 820–830, 2016. [8] I. U. Arachchige and M. G. Kanatzidis, “Anomalous band gap evolution from band inversion in Pb1- x Snx Te Nanocrystals 2009,” Journal Title, vol. #, no. #, pp. xx–xx, 2009. [9] R. Venkatasubramanian, E. Siivola, T. Colpitts, and B. O’Quinn, “Thin-film thermoelectric devices with high room temperature figures of merit,” Nature, vol. 413, no. 6856, pp. 597–602, 2001.
[10] W. Kobayashi, W. Tamura, and I. Terasaki, “Thermal conductivity and dimensionless figure of merit of thermoelectric rhodium oxides measured by a modified harman method,” J. Electron. Mater., vol. 38, no. 7, pp. 964–967, 2009.
[11] H. Iwasaki, H. Morita, and Y. Hasegawa, “Evaluation of thermoelectric properties in Bi-microwires by the Harman method,” Jpn. J. Appl. Phys., vol. 47, no. 5 PART 1, pp. 3576–3580, 2008.
[12] J. De Boor and V. Schmidt, “Complete characterization of thermoelectric materials by a combined van der Pauw approach,” Adv. Mater., vol. 22, no. 38, pp. 4303–4307, 2010.
[13] M. J. Anderson and P. J. Whitcomb, DOE Simplified, Third. 2007.